Ebalta MG 128 / Comp. A+B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UY4xYX_Ebalta-MG-128-Comp-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta MG 128 is processed on a two-component low pressure device. After grinding with a sand paper , grit 280, the surface can be varnished with a commercial lacquer. For better adhesion we recommend the use of a primer coat. Nitrocellulose lacquers have a better adhesion on polyurethane surfaces than on acryl-lacquer-systems. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 to 85 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2500 to 3000 | MPa | ISO 178 |
| Flexural Stress | 102 to 122 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 31 to 45 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 78.0 to 84.0 | °C | ISO 75-2/B |
| Glass Transition Temperature | 100 | °C | DSC |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 91 Mix Ratio by Weight: 110 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.14 to 1.18 | g/cm³ | |
| Viscosity (25°C) | 0.85 to 1.2 | Pa·s | |
| Curing Time (20°C) | 3.0 to 3.5 | hr | |
| Pot Life 1(20°C) | 6.0 to 7.0 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN G-153 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| RTV-2 XP-382 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Ultradur® B 4040 G11 HMG BK15029 | BASF Corporation | PBT | Ultradur® |
| Fainplast PVC RK 321 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Hapflex™ 673-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |