CYCOLOY™ CY6110 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UXDq9M_CYCOLOYCY6110resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow / impact balance for a wide variety of thin wall or large size applications including business equipment, enclosures, among others. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 23.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2750 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 63.9 | MPa | ASTM D638 |
| Yield | 63.1 | MPa | ISO 527-2/50 |
| Fracture 3 | 47.5 | MPa | ASTM D638 |
| Fracture | 46.4 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.1 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture 5 | 65 | % | ASTM D638 |
| Fracture | 35 | % | ISO 527-2/50 |
| Flexural Modulus 6 | 2440 | MPa | ISO 178 |
| Flexural Stress | 94.5 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 7 | 10 | kJ/m² | ISO 179/1eA |
| 23°C 8 | 33 | kJ/m² | ISO 179/1eA |
| 23°C 9 | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 100 | J/m | ASTM D256 |
| 23°C | 480 | J/m | ASTM D256 |
| -30°C 10 | 12 | kJ/m² | ISO 180/1A |
| -30°C 11 | 10 | kJ/m² | ISO 180/1A |
| 23°C 12 | 45 | kJ/m² | ISO 180/1A |
| 23°C 13 | 23 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 14 | |||
| 0.45 MPa, unannealed, 64.0mm span | 98.6 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 88.1 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/B50 |
| -- | 106 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.0E-6 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 85.0 | °C | UL 746 |
| RTI Imp | 85.0 | °C | UL 746 |
| RTI | 85.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 46 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 31 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.90 | IEC 60250 | |
| 60 Hz | 2.90 | IEC 60250 | |
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 2.0E-3 | IEC 60250 | |
| 60 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 7.0E-3 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.50 mm | 5VB | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 825 | °C | IEC 60695-2-13 |
| 2.00 mm | 825 | °C | IEC 60695-2-13 |
| 3.00 mm | 825 | °C | IEC 60695-2-13 |
| Oxygen Index | 31 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 230 - 280 | °C | |
| Middle Temperature | 240 - 290 | °C | |
| Front Temperature | 250 - 300 | °C | |
| Nozzle Temperature | 250 - 300 | °C | |
| Processing (Melt) Temp | 250 - 300 | °C | |
| Mold Temperature | 60.0 - 85.0 | °C | |
| Vent Depth | 0.030 - 0.075 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 80*10*3 sp=62mm |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ARE-55D | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| NITRIFLEX LVP-106 | NITRIFLEX | SBR, Unspecified | NITRIFLEX |
| HIPLEX® HMN 6050 | HIP-PetroHemija | HDPE | HIPLEX® |
| Karina CLEAR PVC COMPOUND -E 75/313-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| Deprene 101-35 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |