Petra® 130 FR BK-112
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Petra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UX36f6_Petra-130-FR-BK-112.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Petra 130 FR BK-112 is a 30% glass fiber reinforced, black pigmented, flame retardant injection molding compound based on post-consumer and post-industrial recycle polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. Applications Petra 130 FR BK-112 is generally recommended for applications such as electrical housing and bobbins. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Break, -40°C | 170 | MPa | |
| Break, 23°C | 125 | MPa | |
| Break, 80°C | 75.0 | MPa | |
| Break, 121°C | 50.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, -40°C | 1.7 | % | |
| Break, 23°C | 2.0 | % | |
| Break, 80°C | 4.4 | % | |
| Break, 121°C | 5.6 | % | |
| Flexural Modulus (23°C) | 9700 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 245 | °C | ASTM D3418 |
| CLTE - Flow | 2.4E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | ||
| 0.300 mm | 75.0 | °C | |
| 0.750 mm | 155 | °C | |
| 1.50 mm | 155 | °C | |
| 3.00 mm | 155 | °C | |
| RTI Imp | UL 746 | ||
| 0.300 mm | 75.0 | °C | |
| 0.750 mm | 155 | °C | |
| 1.50 mm | 155 | °C | |
| 3.00 mm | 155 | °C | |
| RTI Str | UL 746 | ||
| 0.300 mm | 75.0 | °C | |
| 0.750 mm | 155 | °C | |
| 1.50 mm | 155 | °C | |
| 3.00 mm | 155 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.300 mm | V-0 | ||
| 0.750 mm | V-0 5VA | ||
| 1.50 mm | V-0 5VA | ||
| 3.00 mm | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 100 to 110 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mecoline I RDX 5244 F | Melos GmbH | Fluorelastomer | Mecoline |
| CP PRYME® Polypropylene PPH100-18M | Chase Plastics Services Inc. | PP Homopolymer | CP PRYME® Polypropylene |
| IPC PP 4830H-MLGF8-R2-UV | International Polymers Corporation | PP, Unspecified | IPC PP |
| PENTAMID AHT GV30 H1 schwarz | PENTAC Polymer GmbH | Nylon 46 | PENTAMID AHT |
| Sylvin 8864-70D Brown 7398 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |