Selvol™ E 107
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | Sekisui Chemical Company, Ltd. |
| Trademark: | Selvol™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UWcQSA_Selvol-E-107.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SELVOL™ E 107 is a low viscosity fully hydrolysed polyvinyl alcohol which finds applications principally in the Adhesive, Paper and Textile industries. Adhesives: PVAc Emulsions for wood,paper, packaging and building. Paper: Surface sizing ; Pigment coating ; Thermal paper ; Antigrease treatment. Textiles: Cotton yarn sizing ; Spun yarn sizing ; Finishing ; Non wovens. Others: Ceramics binder and coating ; Water soluble films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 to 1.31 | g/cm³ | |
| Ash Content - Expressed as Sodium Oxide | < 1.2 | wt% | Internal Method |
| pH - Of a 4% aqueous solution 1 | 5.0 to 7.0 | Internal Method | |
| Viscosity - Of a 4% aqueous solution at 20ºC 2 | 6 to 7 | mPa·s | Brookfield |
| VOC Content | < 1.0 | wt% | Internal Method |
| Optical | Nominal Value | ||
|---|---|---|---|
| Refractive Index - nD^20°C | 1.5200 to 1.5500 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degree of Hydrolysis | 98.0 to 98.8 | mol% | Internal Method |
| Light Stability | Excellent | ||
| Methanol Content | < 0.9 | wt% | Internal Method |
| Volatiles | < 5.0 | wt% | Internal Method |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | 85.0 | °C | |
| Melting Temperature | 230 | °C | |
| CLTE - Flow (0 to 45°C) | 7.0E-5 to 1.0E-4 | cm/cm/°C | |
| Specific Heat | 1650 to 1670 | J/kg/°C | |
| Thermal Conductivity | 2.0 | W/m/K |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Volume Resistivity | 3.1E+7 to 3.8E+7 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | International Reference: ISO 976 |
| 2 . | International Reference: ISO 2555 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| GAPEX® RPP20EB71GY GRAY | Ferro Corporation | PP Homopolymer | GAPEX® |
| LUVOCOM® 1-8385 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Durethan® DP 1801/30 H3.0 000000 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |
| CYCOLAC™ EX39F resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Moplen HP550J | LyondellBasell Industries | PP Homopolymer | Moplen |