LNP™ LUBRICOMP™ OFL36A compound
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UWMNMd_LNP-LUBRICOMP-OFL36A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP OFL36A is a compound based on PPS - Branched resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound OFL-4036 Product reorder name: OFL36A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 to 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 to 0.48 | % | ISO 294-4 |
| Flow : 24 hr | 0.13 to 0.18 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12300 | MPa | ASTM D638 |
| -- | 11100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 145 | MPa | ASTM D638 |
| Break | 124 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.7 | % | ASTM D638 |
| Break | 1.4 | % | ISO 527-2 |
| Flexural Modulus | 11000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| -- | 200 | MPa | ASTM D790 |
| -- | 197 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.44 | ||
| vs. Itself - Static | 0.35 | ||
| Wear Factor - Washer | 33.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C 2 | 9.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D4812 |
| 23°C 3 | 26 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.40 | J | ASTM D3763 |
| -- | 1.97 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 269 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 266 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT GP2057F | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| TECHNYL STAR™ SX 216 V60 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| Fainplast PVC KLT 87/UV | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| DURACON® GH-10 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| INELEC PEICF20 | Infinity LTL Engineered Compounds | PEI | INELEC |