Sindustris PC GP5007B
| Category: | PC , Polycarbonate |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UVb0Sg_Sindustris-PC-GP5007B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sindustris PC GP5007B is a Polycarbonate (PC) material. It is available in Asia Pacific for injection molding. Primary attribute of Sindustris PC GP5007B: High Flow. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 55.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 90.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 290 | J/m | |
| 23°C, 3.20 mm | 570 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 114 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 245 to 275 | °C | |
| Front Temperature | 245 to 275 | °C | |
| Nozzle Temperature | 245 to 275 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ A70 TM-Y H NC121 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Durolon® V2200 | Unigel Plásticos | PC | Durolon® |
| IROCOAT® CA-128 | Huntsman Corporation | TPU, Unspecified | IROCOAT® |
| KEBAFORM® C 6027 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Softell DKG100N | LyondellBasell Industries | TPO (POE) | Softell |