LG ABS XR474
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UVKLYW_LG-ABS-XR474.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Heat Resistance Applications Automotives Interior & Exterior Housing |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 47.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 15 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 76.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 59 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 49 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 140 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm, injection molding | 112 | °C | ASTM D648 |
| 0.45 MPa, annealed, 6.40mm | 120 | °C | ASTM D648 |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 5 |
| RTI Elec (3.00 mm) | 60.0 | °C | UL 746 |
| RTI Imp (3.00 mm) | 60.0 | °C | UL 746 |
| RTI (3.00 mm) | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 180 - 220 | °C | |
| Middle Temperature | 200 - 220 | °C | |
| Front Temperature | 220 - 230 | °C | |
| Nozzle Temperature | 220 - 230 | °C | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Back Pressure | 0.981 - 2.94 | MPa |
| Injection instructions |
|---|
| Minimum Moisture Content: <0.07% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Proteus® O & P | Quadrant Engineering Plastic Products | PP Homopolymer | Quadrant EPP |
| TRIREX® Compound 3025M10 | Samyang Corporation | PC | TRIREX® Compound |
| Unichem 6574 | Colorite Polymers | PVC, Unspecified | Unichem |
| Dryflex® 500300S | ELASTO | SEBS | Dryflex® |
| Karina GREEN COLOR CONCENTRATE -E 40/551-RG-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |