Multilon® TN-7000F
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Multilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UUazTu_Multilon-TN-7000F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS polymer alloy, Non-halogen type flame resistant series |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.40 to 0.60 | % | |
| Flow : 4.00 mm | 0.40 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 63.0 | MPa | |
| Break | 46.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 2.0 | % | |
| Break | 20 | % | |
| Flexural Modulus 1 | 3200 | MPa | ISO 178 |
| Flexural Stress 2 | 96.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 94.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 84.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 97.0 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 6.0E-5 | cm/cm/°C | |
| Transverse | 7.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.20 mm | V-0 | ||
| 1.80 mm | 5VB |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R543H | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Nanjing Hongrui PC CT1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC | Nanjing Hongrui PC |
| Amilan® CM3004G-30 | Toray Resin Company | Nylon 66 | Amilan® |
| LNP™ COLORCOMP™ E1000CE compound | SABIC Innovative Plastics | PEI | LNP™ COLORCOMP™ |
| TechnoMid PA6 S GF 50 | TechnoCompound GmbH | Nylon 6 | TechnoMid |