Lotryl® 24MA005
| Category: | EMA , Ethylene Methyl Acrylate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotryl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UUGKwv_Lotryl-24MA005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTRYL® 24MA005 is a random copolymer of Ethylene and Methyl Acrylate produced by high-pressure radicalar polymerization process. Applications Due to the methyl acrylate content, LOTRYL® 24MA005 can be used for applications where softness, flexibility and polarity are required. Typical applications are flexible film, polyesters modification and cable compounds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 to 0.60 | g/10 min | ASTM D1238, ISO 1133 |
| Methyl Acrylate Content | 23.0 to 26.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 84 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 17.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 750 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (Compression Molded) | 18.0 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 45.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 72.0 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 to 170 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Die Temperature | 170 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 AFA-6145 V0 | RTP Company | PPA | RTP |
| SCANAMID 66 A33^E F30 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Forprene® 6NE901A90 | SO.F.TER. SPA | TPV | Forprene® |
| HiPrene® MT42HS | GS Caltex | PP, Unspecified | HiPrene® |
| OP - PC/PBT 802-I | Oxford Polymers | PC+PBT | OP - PC/PBT |