PETLIN LD M022X
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | PETLIN (MALAYSIA) SDN BHD |
| Trademark: | PETLIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UUFm6D_PETLIN-LD-M022X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETLIN LD M022X is a low density polyethylene resin designed primarily for injection molding and masterbatch applications. It is produced by the state-of-the-art Clean Tubular Reactor production technology. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 45 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 175 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 8.00 | MPa | |
| Break | 7.00 | MPa | |
| Tensile Strain (Break) | 400 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 82.0 | °C | ISO 306 |
| Melting Temperature (DSC) | 105 | °C | DIN 53765 |
| Peak Crystallization Temperature (DSC) | 100 | °C | DIN 53765 |
| Heat of Fusion | 122 | J/g | DIN 53765 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Comco PA 6/12 G | Comco-Plastic GmbH | Nylon 6/12 | Comco |
| Karina CLEAR PVC COMPOUND 65/200-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polimid A 30 GF | Poliblend S.p.a. | Nylon 66 | Polimid A |
| Braskem PE HF2208S3 | Braskem | LLDPE | Braskem PE |
| OTECH ALLOY OW225XF - Cord Insulation | OTECH Corporation | TP, Unspecified | OTECH ALLOY |