Quadrant EPP PPS Compression
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UU9e0v_Quadrant-EPP-PPS-Compression.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Quadrant EPP PPS Compression is a Polyphenylene Sulfide (PPS) product. It can be processed by compression molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.020 | % | |
| Saturation | 0.030 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 93 | ||
| R-Scale | 125 | ||
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2240 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 2550 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 124 | MPa | ASTM D790 |
| Compressive Modulus | 2830 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 124 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Steel - Static) | 0.40 | Internal Method | |
| Wear Factor | 4000 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 121 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 218 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.105 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 282 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.29 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | > 1.0E+13 | ohms | Internal Method |
| Dielectric Strength 4 | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.3E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| 4 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ C400HD | Mando Advanced Materials Co., Ltd. | LCP | SEPAZ™ |
| Dorlyl PVC FC 37B | DORLYL S.N.C. | PVC, Unspecified | Dorlyl PVC |
| Huafon EP158 | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| KumhoSunny ABS HU650Z | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Hostacom G3 R05N 105555 BLK | LyondellBasell Industries | PP, Unspecified | Hostacom |