Quadrant EPP TIVAR® CleanStat™
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UTygWG_Quadrant-EPP-TIVAR-CleanStat-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tivar® CleanStat™ meets requirements of FDA regulation 21CFR177.1520, item 2.1 and 2.2, for articles intended for direct and indirect food contact usage and regulation 21CFR178.3297 governing pigments and food contact usage. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | < 0.010 | % | |
| Saturation | < 0.010 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 745 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 35.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 200 | % | ASTM D638 |
| Flexural Modulus | 758 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 22.1 | MPa | ASTM D790 |
| Compressive Modulus | 536 | MPa | ASTM D695 |
| Compressive Strength (10% Strain, 23°C) | 21.4 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Steel - Static) | 0.12 | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 46.7 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 82 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.0701 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 135 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 3.4E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 to 1.0E+10 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Torelina® A400M-X05 | Toray Resin Company | PPS | Torelina® |
| UBESTA 3030 JI9L | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| EMOPLEN® CP GFR 20 FR V0 | EMAS Plastik San.Tic.AS. | PP Copolymer | EMOPLEN® |
| LUVOCOM® 1-8973/LGF | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| SABIC® PC PC0700 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |