Arlon® 35N
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | Arlon-MED |
| Trademark: | Arlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UTTlaM_Arlon-35N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35N is a pure polyimide laminate and prepreg system for applications requiring high temperature performance. High Tg (250°C) results in low Z-direction expansion for resistance to PTH failure during PWB processing, and minimizes risk of latent PTH defects in-service. Reduced temperature and time to cure offers improved throughput compared to traditional polyimide cycles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.60 | g/cm³ | ASTM D792A |
| Water Absorption (24 hr) | 0.26 | % | Internal Method |
| Decomposition Temperature | Internal Method | ||
| 5% | 407 | °C | |
| Intial | 363 | °C |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | Internal Method | ||
| -- 2 | 1.1 | kN/m | |
| -- 3 | 1.1 | kN/m | |
| -- 4 | 1.0 | kN/m |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Expansion Rate (50 to 260°C) 5 | 1.2 | % | Internal Method |
| T260 | > 1.0 | hr | Internal Method |
| T288 | > 1.0 | hr | Internal Method |
| T300 | 11.0 | min | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 22100 | MPa | Internal Method |
| Poisson's Ratio 6 | 0.15 | ASTM D3039 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | > 250 | °C | Internal Method |
| CLTE - Flow | |||
| -- 7 | 1.6E-5 | cm/cm/°C | Internal Method |
| < 250°C 8 | 5.1E-5 | cm/cm/°C | Internal Method |
| > 250°C 9 | 1.6E-4 | cm/cm/°C | Internal Method |
| Thermal Conductivity (100°C) | 0.20 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | Internal Method | ||
| -- 10 | 3.7E+14 | ohms | |
| -- 11 | 5.0E+14 | ohms | |
| Volume Resistivity | Internal Method | ||
| -- 12 | 1.2E+14 | ohms·cm | |
| -- 13 | 1.6E+14 | ohms·cm | |
| Dielectric Strength | 56 | kV/mm | Internal Method |
| Dielectric Constant (1 MHz) | 4.20 | Internal Method | |
| Dissipation Factor (1 MHz) | 0.010 | Internal Method | |
| Arc Resistance | 165 | sec | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-1 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | After Thermal Stress |
| 3 . | At Elevated Temperatures |
| 4 . | After Process Solutions |
| 5 . | Z-Axis |
| 6 . | x and y direction |
| 7 . | Y-axis |
| 8 . | Z-axis |
| 9 . | Z-axis |
| 10 . | E24/125 |
| 11 . | C96/35/90 |
| 12 . | E24/125 |
| 13 . | C96/35/90 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® B240MN | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| TAIRILAC AF3500 | Formosa Plastics Corporation | ABS | TAIRILAC |
| Braskem PP TI4003F | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| apigo bio® CM 680 | API SpA | TPO (POE) | apigo bio® |
| Sylvin 9762-66 White 1566 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |