Vydyne® R533H BK0667
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UTIT8R_Vydyne-R533H-BK0667.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vydyne R533H BK0667 is a black, 33% glass-filled polyamide resin for injection molding designed specifically to withstand exposure to calcium chloride for extended periods of time. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 0.90 | -- | % | |
| Flow : 23°C, 2.00 mm | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.80 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10700 | 6200 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 190 | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.8 | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9400 | 5300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 270 | 120 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | 8.0 | kJ/m² | |
| 23°C | 11 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 64 | 64 | kJ/m² | |
| 23°C | 73 | 79 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 12 | 14 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 1.8E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 8.3E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarFlex P 7350-9000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | Starflex |
| Kingfa JH960 HT10 | Kingfa | PC+ABS | Kingfa |
| Hostaform® C13031 XF | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LNP™ VERTON™ RV00CEXP compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ VERTON™ |
| POLYfill PP HIP8040 VT2 | Polykemi AB | PP, Unspecified | POLYfill |