Kepital® TE-33A
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | KEP Americas |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | USp5hn_KepitalTE33A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A toughened, low-viscosity grade for general injection molding. Suitable for applications requiring higher impact resistance, impact noise, and quality surface. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 44.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 35 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1750 | MPa | ISO 178 |
| Flexural Stress (23°C) | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 165 | °C | ISO 11357-3 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1005 FR UV | RTP Company | PBT | RTP |
| Vi-Chem PVC VNC66-30I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| WPP PP PPH3TF4-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| NEFTEKHIM ABS 0445E | Nizhnekamskneftekhim Inc. | ABS | NEFTEKHIM ABS |
| Sylvin 9915-87 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |