HOPELEN FO-135
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HOPELEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | URUxLZ_HOPELEN-FO-135.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HOPELEN FO-135 is homo polymer resin produced by the polymerization of propylene. This grade is designed to be processed in BOPP film applications. This grade shows good transparence, anti-static and printing properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 34.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 1470 | MPa | ASTM D790 |
| Coefficient of Friction (Cast Film) | < 1.0 | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 149 | °C | ASTM D1525 |
| Peak Melting Temperature | 160 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm, Cast Film) | < 0.90 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 4120-64A | Vi-Chem Corporation | TPE | Sevrene® |
| TAROMID A 280 R1 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 2070Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| Alathon® L5008HP | LyondellBasell Industries | HDPE, HMW | Alathon® |
| Epocast 1618 D/B | Huntsman Advanced Materials | Epoxy | Epocast |