FRblend® PBT-2500
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | FRblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UQydp6_FRblend-PBT-2500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FRblend® PBT-2500 is unfilled, flame retardant polybutylene-terephalate compound. The flame retardant system is based on halogen-free flame retardant. This grade offers good mechanical properties and heat stability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 to 1.7 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3420 | MPa | ASTM D638 |
| Tensile Strength | 53.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 18 | % | ASTM D638 |
| Flexural Modulus | 2630 | MPa | ASTM D790 |
| Flexural Strength | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 72.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Nylon 5034 B | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| Formolene® HB6007 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| IZTAVIL P-225-1 GP | Mexichem Corporativo | PVC Homopolymer | IZTAVIL |
| KEBAFORM® C 8027 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Sylvin 9787-75 Grey 9620 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |