SCHULAMID® 12 GF 20 H BLACK 96.8001 REC
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UQo4BC_SCHULAMID-12-GF-20-H-BLACK-96-8001-REC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass fiber reinforced and heat stabilized Polyamide 12, recycled grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4000 | 3400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 70.0 | 60.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 5.0 | 7.0 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 14 | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 55 | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 170 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 145 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 175 | -- | °C | ISO 306/A50 |
| -- | 155 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 50 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | IEC 60695-11-10, -20 | |
| 3.00 mm | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 725 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 725 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 750 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 750 | -- | °C | IEC 60695-2-13 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLPLAST TC 5000A | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| Gallonprene® GP540-8502(n)F | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Ecomann® Bioresin EM20010 | Shenzhen Ecomann Biotechnology Co., Ltd. | PHA | Ecomann® |
| Karina GRAY PVC COMPOUND 700-DA-18/291-Y-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ DF004 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |