VECTRA® E845i LDS
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UPHDoV_VECTRA-E845i-LDS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDS capable LCP with higher DTUL and impact Chemical abbreviation according to ISO 1043-1: LCP Inherently flame retardant UL-Listing V-0 in black at 0.25mm thickness per UL 94 flame testing. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.77 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.23 | % | ISO 294-4 |
| Flow direction | 0.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 14000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 255 | °C | ISO 75-2/A |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 8.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity | |||
| 1 MHz | 3.87 | IEC 60250 | |
| 2.05 GHz | 4.35 | IPC TM-650 2.5.5.13 | |
| Dissipation Factor | |||
| 1 MHz | 0.037 | IEC 60250 | |
| 2.05 GHz | 5.0E-3 | IPC TM-650 2.5.5.13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 315 - 325 | °C | |
| Middle Temperature | 320 - 330 | °C | |
| Front Temperature | 325 - 335 | °C | |
| Nozzle Temperature | 340 - 350 | °C | |
| Processing (Melt) Temp | 340 - 350 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 50.0 - 150 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 340 to 350°CZone 4 Temperature: 335 to 345°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® SX01 | Toray Resin Company | Nylon 6+ABS | Toyolac® |
| Unichem 1116G-015 | Colorite Polymers | PVC, Flexible | Unichem |
| Pibiter® NRV10 NATURALE | SO.F.TER. SPA | PBT | Pibiter® |
| ISOTHANE® 1085A-FR | Great Eastern Resins Industrial Co., Ltd. (GRECO) | TPU-Polyester | ISOTHANE® |
| Abstron KU602M | Bhansali Engineering Polymers Limited | ABS | Abstron |