AXELERON™CS B- 6005 NT is a high molecular weight, low density polyethylene insulation material, which combines mechanical and electrical properties well, making it suitable as the main dielectric material. AXELERON™CS B- 6005 NT meets the following raw material specifications:
|
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, F20) | > 96.0 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 15.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -90.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (-5°C) | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(3.18 mm) | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.28 | ASTM D1531 | |
| Dissipation Factor (1 MHz) | 2.0E-4 | ASTM D1531 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 191 - 218 | °C |
| Extrusion instructions |
|---|
| AXELERON™ CS 6005 NT CPD provides excellent surface finish and outstanding output rates over a broad range of conditions. For optimum results, use melt extrusion temperatures in the suggested range of 375 to 425°F (191 to 218°C). However, specific recommendations for processing conditions can be determined only when the application and type of processing equipment are known. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKASTER™ F10G15 | Mando Advanced Materials Co., Ltd. | PBT | TEKASTER™ |
| Wondel® B BN0 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 6 | Wondel® B |
| AKROMID® A3 GF 35 S1 black (2717) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| MAJORIS DG407X - 8784 | AD majoris | PP, Unspecified | MAJORIS |
| VALOX™ 815 resin | SABIC Innovative Plastics | PBT | VALOX™ |