AKROMID® A3 GK 30 black (2306)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UOngrK_AKROMID-A3-GK-30-black-2306-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GK 30 black (2306) is a 30% glass bead filled polyamide 6.6 with low warpage and high surface appearance Application areas are highly integrated housings in the appliance industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.3 | % | |
| Flow | 1.1 | % | |
| Water Absorption (Saturation, 23°C) | 5.8 | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 2.0 | % | ISO 1110 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 30 | % | ISO 1172 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 7.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 28 | kJ/m² | ISO 179/1eU |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 1(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E385PUOO | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| apilon 52® D1 45L | API SpA | TPU-Polyester | apilon 52® |
| Exxtral™ Performance Polyolefin CMU201 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| LNP™ STAT-KON™ MD000IS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |
| LEXAN™ XHT5141 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |