PLUSTEK RA353M8
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UOKyU3_PLUSTEK-RA353M8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% MINERAL FILLED POLYAMIDE 66, TO INCREASE DIMENSIONAL STABILITY. FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.50 to 1.0 | % | ASTM D955 |
| -- | 0.50 to 1.0 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 4.5 | % | ASTM D570 |
| Saturation, 23°C | 4.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 75.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5100 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 145 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 60 | J/m | ASTM D256 |
| 23°C | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 235 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3417 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® 5321-851E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| AKROMID® B3 GF 20 natural (2470) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Gallonprene® GP640-6501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Jackdaw PLA HT16WT6652 | Jackdaw Polymers | PLA | Jackdaw PLA |
| TECACOMP® PPA LDS black 4109 | Ensinger GmbH | PPA | TECACOMP® |