BJB Polyurethane WC-765 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UOGwAz_BJB-Polyurethane-WC-765-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WC-765 A/B is a two part, clear, colorless 65 Shore D urethane castable product that is commonly used to make clear or tinted parts of all kinds. When used at room temperature, castings 1/8" thick or larger can be readily cast. Castings that are less than 1/8" thick generally require a mild post-cure. This product may exhibit a slight yellowing or color change when exposed to direct UV light. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A | 1.077 | g/cm³ | |
| Part B | 1.027 | g/cm³ | |
| Shrinkage | 0.40 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Demold Time (24°C) | 6.0 to 8.0 | hr | |
| Gel Time | 20.0 | min | |
| Work Time (25°C) 1 | 15.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brookfield Viscosity | |||
| Mixed : 25°C | 600 to 700 | mPa·s | |
| Part A : 25°C | 650 | mPa·s | |
| Part B : 25°C | 550 | mPa·s |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 to 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 214 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 31.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 230 | % | ASTM D638 |
| Flexural Modulus | 200 | MPa | ASTM D790 |
| Flexural Strength | 2.17 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 80.6 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 480 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 75, Mix Ratio by Volume: 72 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk |
| Note Message | |
|---|---|
| 1 . | 100 g mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V937 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| ALCOM® PA6 900/8 GF10 MR20 SV1285-04MCF | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Globalene® HP600S | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| KEBAFLEX® SG 85 A.1 | BARLOG plastics GmbH | TES | KEBAFLEX® |
| Durethan® B 35 FA 000000 | LANXESS Corporation | Nylon 6 | Durethan® |