Promyde® B30 P2 GFC30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | NUREL, S.A. |
| Trademark: | Promyde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UMRN61_PromydeB30P2GFC30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Promyde® B30 P2 GFC30 is a Polyamide 6 injection moulding grade with 30% glass and heat stabilised. This material is suitable for Food Contact applications. CHARACTERISTICS This material is distinguished by high mechanical strength, hardness, rigidity, themostability (melting point 220°C), and resistance to hot lubricants and water. Parts made from Promyde® B30 P2 GFC30 have particularly high dimensional stability and creep strength. This material is suitable for Food Contact applications. APPLICATIONS High variety of applications field wherever mechanical properties in combinations with thermal resistance is needed. Glass-fiber reinforced grade are suitable for industrial items such as automotive cooling water tanks, lamp socket housings, fans as well as electrical insulating parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 45.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.40 - 0.45 | -- | % | ISO 294-4 |
| Flow | 0.30 - 0.35 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.7 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| Viscosity Number 1 | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9300 | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 190 | 110 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 3.0 | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 8000 | 5100 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 250 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 13 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 85 | 95 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 4 | 222 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 6.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.80 | 6.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.023 | 0.22 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.6 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Back pressure: moderate |
| Note Message | |
|---|---|
| 1 . | 25°C |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® PTFE 6CN X | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| Tenopom® POM B3 ST PRTA010 PR325 MSP | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| Vinnolit® E 74 CC | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Electrafil® POM CO AS | Techmer Engineered Solutions | Acetal (POM) Copolymer | Electrafil® |
| MACOMASS PVC RAU-PVC 6000 | MACOMASS Verkaufs AG | PVC, Flexible | MACOMASS PVC |