apilon 52® TLE 40
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | API SpA |
| Trademark: | apilon 52® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UMKKqG_apilon-52-TLE-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
apilon 52®TLE 40 is a thermoplastic polyurethane elastomer (polyether)(TPU-polyether) product,. It can be processed by extrusion and is available in Europe. apilon 52®The application areas of TLE 40 include engineering/industrial accessories, electrical/electronic applications, electrical appliances, tools and home applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 15 seconds | 90 | ASTM D2240 | |
| Shaw D, 3 seconds | 40 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 40.0 | MPa | ASTM D638 |
| 100% strain | 8.00 | MPa | ASTM D638 |
| 300% strain | 18.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Flexural Modulus | 50.0 | MPa | ASTM D790 |
| Abrasion Resistance | 50.0 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 100 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-20°C) | No Break | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 110 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 180 - 190 | °C | |
| Middle Temperature | 185 - 200 | °C | |
| Front Temperature | 190 - 215 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Back Pressure: Medium to LowLocking Pressure: High |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 110 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Cylinder Zone 1 Temp. | 160 - 185 | °C | |
| Cylinder Zone 2 Temp. | 170 - 200 | °C | |
| Cylinder Zone 3 Temp. | 175 - 210 | °C | |
| Cylinder Zone 4 Temp. | 180 - 220 | °C | |
| Die Temperature | 170 - 210 | °C |
| Extrusion instructions |
|---|
| L/D Ratio: 20:1 to 30:1Compression Ratio: 1:2.5 to 1:3 |
| Note Message | |
|---|---|
| 1 . | Without Notch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2404AF00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TRIREX® 3027U(H) | Samyang Corporation | PC | TRIREX® |
| WINTEC™ WFW4F | Japan Polychem Corporation | PP Random Copolymer | WINTEC™ |
| Europrene® N 2860 | Versalis S.p.A. | NBR | Europrene® |
| Osterlene® PPC-57-1.4-N | Osterman & Company | PP Impact Copolymer | Osterlene® |