Novalloy-A A2506
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ULp3ZR_Novalloy-A-A2506.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-A A2506 is an Acrylonitrile Butadiene Styrene + Nylon (ABS+Nylon) material. It is available in Asia Pacific. Primary attribute of Novalloy-A A2506: Flame Rated. |
| General Information |
|---|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.28 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.50 | -- | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.50 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | 115 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Yield) | 110 | 88.0 | MPa | ISO 527-2 |
| Flexural Modulus | 720 | 6000 | MPa | ISO 178 |
| Flexural Stress | 180 | 146 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 15 | 16 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | |||
| -30°C, 6.40 mm | 100 | -- | J/m | |
| 23°C, 6.40 mm | 150 | 180 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed, 6.40 mm | 205 | 190 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 205 | 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 160 | 140 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 160 | 150 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Moisture Content | -- | 0.70 | % |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 180 to 210 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HF5255A | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Sinpolene MBB106LE | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| U-polymer U-8000 | UNITIKA Plastics Division | Polyarylate | U-polymer |
| AFLAS® 150C | Asahi Glass Co., Ltd. | Fluorelastomer | AFLAS® |
| Karina GRAY COLOR CONCENTRATE 18/276-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |