EL-Lene™ H5818J
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UL1Sb5_EL-Lene-H5818J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Lene H5818J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flowability grade designed for high productivity requirement. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.962 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 2.00mm | 2.0 | % | ASTM D955 |
| Transverse flow : 2.00mm | 2.5 | % | ASTM D955 |
| Environmental Stress-Cracking Resistance (50°C, 25% Igepal, Compression Molded, F50) | 2.00 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 27.5 | MPa | ASTM D638 |
| Fracture | 15.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 150 | % | ASTM D638 |
| Flexural Modulus | 1270 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 |
| Melting Temperature | 131 | °C | ASTM D2117 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 250 | °C | |
| Mold Temperature | 20.0 - 60.0 | °C | |
| Injection Rate | Fast | ||
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Injection Pressure: 30 to 70% of max. pressurePacking and Holding Pressure: 30 to 50% of max. pressureBack Pressure: 10% of max. pressure |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT1055-685UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Sipolprene® 35150 | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Sumitomo PE B2555 | Sumitomo Chemical Asia | HDPE | Sumitomo PE |
| Mafill® CR C 8041 | Ravago Group | PP Copolymer | Mafill® |
| Petrothene® LR732031 | LyondellBasell Industries | HDPE | Petrothene® |