UBESTA 3035 UF
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBESTA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UKzOD6_UBESTA-3035-UF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UBESTA 3035 UF is a high molecular, non-reinforced and non-plasticized Polyamide 12 specially design for pressurized gas pipes. UBESTA 3035 UF shows only low moisture absorption and therefore exceptional dimension stability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.5 | % | ISO 294-4 |
| Flow direction | 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ISO 2039-2 | |
| Durometer Hardness (Shore D) | 74 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 44.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | ISO 527-2 |
| Fracture | 200 | % | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Flexural Stress | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, complete fracture | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C, complete fracture | 16 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 92.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 46.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 178 | °C | ISO 3146 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Tensile Strain at Break, ISO 527: >200%Abrasion Loss, ISO 9352, CS-17, 1000 rev.: 6 mg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BR3XNT6509 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Karina BLACK PVC COMPOUND 850-48/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sumiliteresin® ECP-147 | SBHPP | Epoxy | Sumiliteresin® |
| ESTOPLAST EP 5010RD14 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| Sylvin 9604-90 Red 6292 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |