Order Products : sales@su-jiao.com
Chemlon® 133 GHU BK155
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UKcWP6_Chemlon-133-GHU-BK155.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Chemlon® 133 GHU BK155 is a Polyamide 66 (Nylon 66) material filled with 33% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Chemlon® 133 GHU BK155: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.15 to 0.40 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 160 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 2.5 | % | |
| Break | 2.5 | % | |
| Flexural Modulus | 8600 | MPa | ISO 178 |
| Flexural Stress | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 7.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 249 | °C | ISO 75-2/A |
| Melting Temperature | 257 | °C | ASTM D789 |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ISO 1325 |
| Dielectric Strength (3.00 mm) | 16 | kV/mm | ASTM D149 |
| Comparative Tracking Index | > 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | HB | UL 94 | |
| Oxygen Index | 25 | % | ISO 4589-2 |
| FMVSS Flammability | PASSED | FMVSS 302 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Color Fastness - delta E after 2500 kJ/m² exposure | < 3.00 | SAE J1960 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 255 to 275 | °C | |
| Middle Temperature | 265 to 290 | °C | |
| Front Temperature | 265 to 305 | °C | |
| Nozzle Temperature | 265 to 295 | °C | |
| Processing (Melt) Temp | 265 to 290 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA/PP 7500 GF 30 | TER HELL PLASTIC GMBH | Nylon 6+PP | TEREZ PA/PP |
| Ecomass® 1950ZC84 | Ecomass Technologies | Nylon 610 | Ecomass® |
| Karina BLACK PVC COMPOUND 750-DM-48/1-B-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 20-8254 | Lehmann & Voss & Co. | PPA | LUVOCOM® |
| LNP™ THERMOCOMP™ LF004E compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |