AKROTEK® PK-VM TM natural (4954)
| Category: | PK-Aliphatic , Polyketone, Aliphatic |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROTEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UKI3gV_AKROTEK-PK-VM-TM-natural-4954-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROTEK® PK-VM TM natural (4954) is an unreinforced, tribologically modified Polyketon with high flowability Applications are mainly components in techanical, tribological engineering and the automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.35 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 120 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.6 | -- | % | |
| Flow | 1.3 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 0.60 to 0.70 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1500 | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 50.0 | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 40 | 40 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1500 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 55.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.0 | -- | kJ/m² | |
| 23°C | 7.0 | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | -- | kJ/m² | |
| 23°C | 100 | 90 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 185 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 220 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9505HF | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| Adell PET WR-36 | Adell Plastics, Inc. | PET | Adell PET |
| Sylvin 6112-85FU Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| StarPet® 8025-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarPet® |
| Sylvin 8394-90C Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |