EXCELLOY CK10G10
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | EXCELLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UK5RQk_EXCELLOY-CK10G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EXCELLOY CK10G10 is a Polycarbonate + ABS (PC+ABS) product filled with 10% glass fiber. It can be processed by injection molding and is available in Asia Pacific or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.40 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 111 | ASTM D785 | |
| R-Scale | 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 58.8 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3330 | MPa | ASTM D790 |
| -- | 3340 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 98.1 | MPa | ASTM D790 |
| -- | 94.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 14 | kJ/m² | ISO 179 |
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 115 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (ALL) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 240 to 280 | °C | |
| Middle Temperature | 240 to 280 | °C | |
| Front Temperature | 240 to 280 | °C | |
| Mold Temperature | 50.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® 42LH-XE-NBK2 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| CYCOLAC™ X11 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Hylon® N2000HL2 | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| INEOS PP N12Z-00 | INEOS Olefins & Polymers USA | PP Impact Copolymer | INEOS PP |
| 3M™ Dyneon™ PTFE Compound PDR 05017 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |