Panlite® BN-8120R
| Category: | PC , Polycarbonate |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Panlite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UGrmnB_Panlite-BN-8120R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon fiber reinforced grades-20% Carbon fiber, Flame resistant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.30 to 0.50 | % | |
| Flow : 4.00 mm | 0.020 to 0.20 | % | |
| Water Absorption (23°C, 24 hr) | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 11500 | MPa | ISO 178 |
| Flexural Stress 2 | 185 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 23 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 149 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 147 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 151 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.0E-5 | cm/cm/°C | |
| Transverse | 6.0E-5 | cm/cm/°C | |
| RTI Elec (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 to 1.0E+2 | ohms | IEC 60093 |
| Volume Resistivity | 10 to 1.0E+3 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-0 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS PP HPP12 | Nexus Resin Group, LLC. | PP Homopolymer | NEXUS PP |
| LNP™ THERMOCOMP™ D251 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |
| Pacrel® 6395N | Nanjing Jinling OPTA Polymer Co., Ltd. | TPV | Pacrel® |
| EPALINE 786A25 | Epaflex Polyurethanes S.R.L. | TPU-Polyether | EPALINE |
| CYCOLOY™ CM6140 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |