TROGAMID® T BX9724
| Category: | Nylon 6/3T , Polyamide 6/3T Copolymer |
| Manufacturer: | Evonik Industries AG |
| Trademark: | TROGAMID® T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UGoeke_TROGAMID-T-BX9724.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TROGAMID® T and BX consist of terephthalic acid and 2,2,4- /2,4,4-trimethyl hexamethylene diamine, a chemical composition that is responsible for their amorphous structure. This makes TROGAMID® T transparent in contrast to the semi-crystalline high-performance plastics of High Performance Polymers. The amorphous structure also results in low molding shrinkage and low tendency to warp. In addition to the basic products, a range of specially equipped compounds is also available. The product line fits a wide range of applications and satisfies many requirement profiles. TROGAMID® BX9724 Polymer blend consisting of amorphous and semi-crystalline polyamides, 40% glass fiber reinforced, with high tensile modulus for injection molding, dimensionally stable even while absorbing water; appropriate for substituting cast metal parts with plastic. Moldings exhibit outstanding surface qualities in spite of their high glass fiber content. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.48 | g/cm³ | ISO 1183 |
| Viscosity Number | 130 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 90 | ISO 868 | |
| Ball Indentation Hardness | 262 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 220 | MPa | ISO 527-2/5 |
| Nominal Tensile Strain at Break | 3.2 | % | ISO 527-2/5 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 9600 | MPa | |
| 1000 hr | 5200 | MPa | |
| Flexural Modulus | 12000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 10 | kJ/m² | |
| 0°C, Complete Break | 11 | kJ/m² | |
| 23°C, Complete Break | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C, Complete Break | 80 | kJ/m² | |
| 0°C, Complete Break | 87 | kJ/m² | |
| 23°C, Complete Break | 96 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 230 | °C | ISO 75-2/B |
| Glass Transition Temperature 1 | 93.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 230 | °C | ISO 306/B |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 2.2E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 3.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 27 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C, 1 MHz) | 6.20 | IEC 60250 | |
| Dissipation Factor (23°C, 1 MHz) | 0.025 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- 2 | 575 | V | |
| Solution A | 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| Glow Wire Flammability Index (1.00 mm) | 750 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 775 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| 2 . | 100 drops value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5195-80 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 916VO-95 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| MAJ'ECO FT100BS - 1199 | AD majoris | Biodeg Polymers | MAJ'ECO |
| SECCO K4912 | Shanghai SECCO Petrochemical Co., Ltd | PP Random Copolymer | SECCO |
| SQUARE® LIM1030-30A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |