MARPOL® LL6R 804UV
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UGKQ8M_MARPOLLL6R804UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MARPOL® LL6R 804UV is a new generation metallocene medium density polyethylene with hexene as comonomer. This is a natural grade available in pellet form. Recommended Applications Intended for the manufacture of rotomolded items |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 10% Igepal, F50 | 155 | hr | ASTM D1693 |
| 100% Igepal, F50 | > 900 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 20.7 | MPa | ASTM D638 |
| Fracture | 11.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 8.0 | % | ASTM D638 |
| Fracture | 300 | % | ASTM D638 |
| Flexural Modulus | 883 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 119 | °C | ASTM D1525 |
| Melting Temperature | 126 | °C | ASTM D3417 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 803 UV | RTP Company | Acetal (POM) Copolymer | RTP |
| SLOVALEN® PC 69 GF 40 | Plastcom | PP, Unspecified | SLOVALEN® |
| TOTAL Polypropylene PPC 4944WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| EPIMIX PBT GV0 30 NC | EPSAN Plastik SAN. ve TiC. A.S. | PBT | EPIMIX |
| SCHULAMID® RD 6 GF 30 | A. Schulman Europe | Nylon 6 | SCHULAMID® |