Andur M-11 (97% HQEE/ 3% TMP)
| Category: | PUR-Ester/MDI , Polyurethane (Polyester, MDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UGCEmM_Andur-M-11-97-HQEE-3-TMP-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur M-11 is an MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in dynamic applications. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 99 | ASTM D2240 | |
| Shaw D | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 2% strain | 3.79 | MPa | ASTM D695 |
| 5% strain | 6.89 | MPa | ASTM D695 |
| 10% strain | 10.3 | MPa | ASTM D695 |
| 15% strain | 13.8 | MPa | ASTM D695 |
| 20% strain | 17.2 | MPa | ASTM D695 |
| 25% strain | 22.1 | MPa | ASTM D695 |
| 50% strain | 67.6 | MPa | ASTM D695 |
| Taber Abrasion Resistance | 47.6 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 22.1 | MPa | ASTM D412 |
| 200% strain | 22.8 | MPa | ASTM D412 |
| 300% strain | 21.7 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 24.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 350 | % | ASTM D412 |
| Compression Set | 33 | % | ASTM D395 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 6.0 - 8.0 | min | |
| Demold Time | 80 | min |
| Additional Information |
|---|
| Die C Tear, ASTM D1004: 900 pliAverage Split Tear, ASTM D1938: 600 pliStoichiometry Curative Level: 90%Parts of curative per 100 parts Andur M-11, 8.9% NCO: 18.76 parts by weightParts of curative per 100 parts Andur M-11, 9% NCO: 18.97 parts by weightParts of curative per 100 parts Andur M-11, 9.1% NCO: 19.18 parts by weightParts of curative per 100 parts Andur M-11, 9.2% NCO: 19.38 parts by weightMix Temperature: Andur M-11: 212°F Curative HQEE/TMP: 230°F Stability: Ambient Temperature, 25°C: 6 Months Melting Temperature, 60°C: 1 Month Processing Temperature, 90°C: 12 Hours Processing Temperature, 105°C: 3 Hours |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 110 - 140 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC PP M1425 | LG Chem Ltd. | PP Impact Copolymer | SEETEC PP |
| BONDYRAM® TL1207 | Polyram Ram-On Industries | PP Copolymer | BONDYRAM® |
| Geon™ Vinyl Flexible R4510H | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Keliren® CM352F | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| Polimid B 30 GF V0A | Poliblend S.p.a. | Nylon 6 | Polimid B |