LNP™ LUBRICOMP™ DBL34 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UFscsF_LNP-LUBRICOMP-DBL34-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Lubricomp* DBL34 is a compound based on Polycarbonate resin containing Glass Bead, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound DBL4034 Product reorder name: DBL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 42.0 | MPa | |
| Break | 40.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 3.1 | % | |
| Break | 4.6 | % | |
| Flexural Modulus 1 | 2900 | MPa | ISO 178 |
| Flexural Stress | 76.0 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.50 | ASTM D3702 Modified | |
| Flexural Strain at Break 2 | 5.3 | % | ISO 178 |
| Wear Factor - Washer | 94.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 137 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 130 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 6.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP212G30V0LG | Kolon Plastics, Inc. | PBT | SPESIN® |
| YUNGSOX® PP 1024 | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| LAMIGAMID® 300 | Schwartz Technical Plastic | Nylon 6 | LAMIGAMID® |
| LNP™ THERMOCOMP™ LC008EXQ compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |
| Sylvin 9789-73 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |