Category: | PC , Polycarbonate |
Manufacturer: | Ginar Technology Co., LTD. |
Trademark: | Kapex |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | UEWMnb_Kapex-C342.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
20% Glass reinforced |
General Information | |
---|---|
Filler / Reinforcement |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
Molding Shrinkage - Flow (1.60 mm) | 0.30 | % | ASTM D955 |
Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Yield) | 117 | MPa | ASTM D638 |
Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
Flexural Modulus | 5860 | MPa | ASTM D790 |
Flexural Strength | 179 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C) | 140 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648 |
Flammability | Nominal Value | Test Method | |
---|---|---|---|
Flame Rating | UL 94 | ||
0.794 mm | HB | ||
1.59 mm | HB | ||
3.18 mm | HB |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
NEOPLAST 180 HOFR | Zylog Plastalloys | TPV | NEOPLAST |
EVICOM™ GA4/526 | INEOS Compounds | PVC, Flexible | EVICOM™ |
Durepol® PBT A3 G15 TZ NTLA010 BT327 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
LUVOCOM® 65-8657 | Lehmann & Voss & Co. | PP Copolymer | LUVOCOM® |
Sylvin 8857-60D Green 3176 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |