Jamplast JPAH
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UDzLFd_Jamplast-JPAH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Jamplast JPAH is an Acetal (POM) Homopolymer material. It is available in North America for cast film, extrusion, injection molding, profile extrusion, or sheet extrusion. Important attributes of Jamplast JPAH are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.20 | % | |
| Saturation, 23°C | 0.72 | % | |
| Equilibrium, 23°C, 50% RH | 0.18 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 2910 | MPa | ASTM D638 |
| Tensile Strength 2(23°C) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C) | 11 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2710 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 31 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 163 | °C | |
| 1.8 MPa, Unannealed | 95.0 | °C | |
| Melting Temperature | 178 | °C | DSC |
| CLTE | ASTM E831 | ||
| Flow : 23 to 54°C | 1.0E-4 | cm/cm/°C | |
| Transverse : 23 to 54°C | 1.0E-4 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 1.50 mm | 105 | °C | |
| 3.00 mm | 105 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 85.0 | °C | |
| 3.00 mm | 85.0 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 90.0 | °C | |
| 3.00 mm | 90.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 210 to 220 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6917 WT020 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Adell Polyamide BT-33 General Purpose | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| Elvaloy® 741 | DuPont Packaging & Industrial Polymers | EVA | Elvaloy® |
| MAJORIS DW374 - 8229 | AD majoris | PP Copolymer | MAJORIS |
| LNP™ KONDUIT™ OX11315 compound | SABIC Innovative Plastics Asia Pacific | PPS | LNP™ KONDUIT™ |