Medalist® MD-215
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Medalist® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UCQ37q_Medalist-MD-215.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This compound is designed for medical and healthcare applications requiring oil resistance. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 3.9 | % | ASTM D955 |
| Transverse flow | 2.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 45 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 1.14 | MPa | ASTM D412 |
| 200% strain | 1.86 | MPa | ASTM D412 |
| 300% strain | 2.79 | MPa | ASTM D412 |
| Tensile Strength (Break) | 2.93 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 350 | % | ASTM D412 |
| Tear Strength | 9.63 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 19 | % | ASTM D395 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 138 - 160 | °C | |
| Middle Temperature | 160 - 182 | °C | |
| Front Temperature | 171 - 193 | °C | |
| Nozzle Temperature | 193 - 216 | °C | |
| Processing (Melt) Temp | 193 - 216 | °C | |
| Mold Temperature | 21.1 - 37.8 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 138 - 149 | °C | |
| Cylinder Zone 2 Temp. | 149 - 160 | °C | |
| Cylinder Zone 3 Temp. | 160 - 182 | °C | |
| Cylinder Zone 5 Temp. | 171 - 193 | °C | |
| Die Temperature | 182 - 204 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecoform® PO30 GB30 NL HS | Eurotec Engineering Plastics | Acetal (POM) Copolymer | Tecoform® |
| SUPREME Specialty PS SP243 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| Di-Pak™ E-4665-3 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| LUVOCOM® 19/XCF/20 | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| EPAMOULD 675A26 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |