RTP 1400 R-5000
| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UCMV5i_RTP-1400-R-5000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (365°C/5.0 kg) | 14 - 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.37 | % | ASTM D570 |
| Moisture Content | 0.040 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2340 | MPa | ASTM D638 |
| Tensile Strength | 69.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 90 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 91.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 209 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+12 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 343 - 388 | °C | |
| Mold Temperature | 138 - 163 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymer-E C7100 | Asia Polymer Corporation (APC) | LDPE | Polymer-E |
| Tarnoform® 200 AR | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Vinnolit® E 74 CC | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| EPO-TEK® H31LV | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LEXAN™ 4704 resin | SABIC Innovative Plastics | PPC | LEXAN™ |