Latan 13 S/15
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UAeXpG_Latan-13-S-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyoximethylene (POM). Glass beads. Medium viscosity. Good dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 2.0 to 2.2 | % | |
| Flow : 2.00 mm | 2.0 to 2.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 3000 | MPa | |
| 60°C | 2000 | MPa | |
| 90°C | 1200 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 50.0 | MPa | |
| Yield, 60°C | 35.0 | MPa | |
| Yield, 90°C | 25.0 | MPa | |
| Break, 23°C | 45.0 | MPa | |
| Break, 60°C | 30.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 8.0 | % | |
| Yield, 60°C | 8.0 | % | |
| Yield, 90°C | 9.0 | % | |
| Break, 23°C | 15 | % | |
| Break, 60°C | 75 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 80.0 | °C | |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 210 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2205 A | RTP Company | PEK | RTP |
| Prime Flexible 7271 CLR | Prime PVC® | PVC, Flexible | Prime Flexible |
| Ultramid® A3X2G5 | BASF Corporation | Nylon 66 | Ultramid® |
| Hostacom PF231-4C | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LNP™ THERMOTUF™ IX02582 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOTUF™ |