LNP™ THERMOCOMP™ WX05505 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UAXG5X_LNP-THERMOCOMP-WX05505-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP WX05505 is a compound based on PBT resin containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound W-5000 Product reorder name: WX05505 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.060 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2510 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 54.0 | MPa | ASTM D638 |
| Yield | 52.0 | MPa | ISO 527-2/5 |
| Break 2 | 36.0 | MPa | ASTM D638 |
| Break | 43.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 3.0 | % | ASTM D638 |
| Yield | 3.2 | % | ISO 527-2/5 |
| Break 4 | 31 | % | ASTM D638 |
| Break | 25 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 2480 | MPa | ASTM D790 |
| -- 6 | 2390 | MPa | ISO 178 |
| Flexural Strength 7(Yield, 50.0 mm Span) | 84.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 51 | J/m | ASTM D256 |
| 23°C 8 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 9 | 100 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 30.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 149 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 56.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 55.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® FC-2 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Unspecified | SILVER® |
| BCC Resins BC 8870 | BCC Products Inc. | TSU | BCC Resins |
| AXELERON™ CS K-3364 NT CPD | The Dow Chemical Company | HDPE | AXELERON™ |
| Lumiloy® GN2206F | LG Chem Ltd. | PPE+PS | Lumiloy® |
| POLYfill PPH K20020 | Polykemi AB | PP Homopolymer | POLYfill |