SOLLAMID B 2700 MW
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Krisoll Resinas Plásticas Ltda. |
| Trademark: | SOLLAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U9VtAV_SOLLAMID-B-2700-MW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The SOLLAMID B 2700 MW 40 contain all the good characteristic properties of polyamide 6. Exhibits excellente behavior in injection without outcrop reinforcement and a high isotropy. The formulas MW are Reinforced with Wollastonita which improves the surface finish and Isotropy Properties. Applications Because of their ease in molding the Sollamid B 2700 MW 40 is suitable for excellent surface finish and paint facility. Large structural parts used mainly in the automotive sector and others too. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.46 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.80 to 1.0 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.90 to 1.0 | -- | % | ASTM D570 |
| Heat Stability | 90 to 100 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 120 | 105 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6700 | 3500 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 90.0 | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | 32 | % | ASTM D638 |
| Flexural Modulus (23°C) | 5800 | 3200 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 150 | 95.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 55 | 95 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 185 | -- | °C | |
| 1.8 MPa, Unannealed | 140 | -- | °C | |
| Melting Temperature | 214 to 220 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+12 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VPA1260 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PCTFE | TEKNIFLEX® |
| Elastollan® C 59 D | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Kumho SBR 1783 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| Iupiace® LV40 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Sylvin 8354-62D Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |