Hostacom D1172 9177
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U9NpHQ_Hostacom-D1172-9177.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% talc filled copolymer,antistatic. Previously known as 2611TC TA4. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 50 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 1650 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 22.0 | MPa | ISO 527-2/50 |
| Flexural Modulus - Secant | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact Strength | ISO 180 | ||
| -30°C | 2.3 | kJ/m² | ISO 180 |
| 23°C | 9.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 55.0 | °C | ISO 306 |
| Additional Information |
|---|
| Coefficient of Linear thermal Expansion, DIN 53752, 23 - 85°C, Parallel: 0.8 1/KFlammability, FMVSS 302: 40 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 830 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Talcoprene® 1540TLT1 NERO | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Tarnamid® T- 27 P | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Texalan® 5 Series 590A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 5 Series |
| NEFTEKHIM PP 1501M | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |