TAROLOX GFR 6
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U8XGsb_TAROLOX-GFR-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT medium viscosity 25% glass fibres reinforced, heat stabilized, halogen free flame retardant UL94 V0, good flame proofing also at low thickness, good flow, good mechanical and thermal properties. High CTI value. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.40 - 0.60 | % | Internal method |
| Flow direction | 0.20 - 0.40 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.050 | % | ISO 62 |
| Saturated, 23°C | 0.22 | % | ISO 62 |
| Granule Humidity 1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 9000 | MPa | ISO 178 |
| Flexural Stress 3 | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -25°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 45 | J/m | ASTM D256 |
| 23°C | 65 | J/m | ASTM D256 |
| Notched Izod Impact (23°C) | 6.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed) | 215 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 208 | °C | ISO 306/B50 |
| Ball Pressure Test (215°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | UL 94 | |
| 0.750 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 120 to 130°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® BF36 L | NUREL, S.A. | Nylon 6 | Promyde® |
| Sumikon® EME-6600CS | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| ACCUTECH™ HP0339G20CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| KEBAFORM® C 90 M | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| LNP™ THERMOCOMP™ KFB11 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |