Horda E8413
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Horda Cable Compounds |
| Trademark: | Horda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U8G2Id_Horda-E8413.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Easy Strippable Semiconductive Shielding E8413 is a crosslinkable easy-strippable semiconductive compound, designed for both XLPE and EPDM rubber insulated cables and use in both dry and steam curing processes. Specifications: E8413 meets the requirements as below, when optimal processing extrusion and end testing procedure are used: AEIC-CS 5/94 BS 6622 HN 33-S-23 (EDF) IEC 502 IEC 840 NF CS 32-223 SS 424 14 16, SS424 14 17 (HD 620 S1:1996) VDE 0273 / 12.87 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ASTM D1928 |
| Mooney Viscosity (ML 1+4, 121°C) | 21 | MU | ISO 289 |
| Moisture Content 1 | < 800 | ppm | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Set (200°C) 2 | 65/10 | % | IEC 60540 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Stripping Angle | 180 | ° | |
| Stripping Force 3 | |||
| EPR : 23°C | 1.5 to 2.0 | kN/m | |
| XLPE : 23°C | 1.0 to 1.5 | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 to 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 11.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 260 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (135°C, 168 hr) | -5.0 | % | ASTM D471 |
| Change in Ultimate Elongation (135°C, 168 hr) | -50 | % | ASTM D471 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | < 5.0E+2 | ohms·cm | |
| 90°C | < 1.0E+3 | ohms·cm | |
| 120°C | < 1.0E+3 | ohms·cm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 40.0 | °C | |
| Hopper Temperature | 23.0 | °C | |
| Cylinder Zone 1 Temp. | 60.0 to 110 | °C | |
| Cylinder Zone 2 Temp. | 60.0 to 110 | °C | |
| Cylinder Zone 3 Temp. | 60.0 to 110 | °C | |
| Cylinder Zone 4 Temp. | 60.0 to 110 | °C | |
| Cylinder Zone 5 Temp. | 60.0 to 110 | °C | |
| Adapter Temperature | 100 to 130 | °C | |
| Die Temperature | 100 to 130 | °C |
| Note Message | |
|---|---|
| 1 . | QAHC-10420 (Karl Fischer method) |
| 2 . | 20 N/cm² |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TOTAL Polyethylene HDPE 5908 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| Chemlon® 109-18 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Desmopan® DP 9665DU | Covestro - PUR | TPU-Polyether | Desmopan® |
| Sylvin 5132-86 Clear Yellow 4174 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |