Styrolution PS 5400/5401
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolution PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U7iENY_Styrolution-PS-5400-5401.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Styrolution PS 5400/5401 is a High Impact Polystyrene product. It can be processed by injection molding or sheet extrusion and is available in Latin America or North America. Applications of Styrolution PS 5400/5401 include medical/healthcare, caps/lids/closures, containers, kitchenware and packaging. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Apparent Density | |||
| -- 1 | 0.59 to 0.64 | g/cm³ | |
| -- 2 | 0.62 to 0.67 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 50 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 20.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 55 | % | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength | 41.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 83.9 | °C | |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 3 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.18 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1.00 mm, 1 MHz) | 2.50 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 25 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 182 to 277 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 to 277 | °C |
| Note Message | |
|---|---|
| 1 . | without external lubricant |
| 2 . | with external lubricant |
| 3 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zenite® 7244 | Celanese Corporation | LCP | Zenite® |
| CP PRYME® Polyethylene PE100HDC-.35FM | Chase Plastics Services Inc. | HDPE | CP PRYME® Polyethylene |
| Lanufene LLF 182N | Ras Lanuf Oil & Gas Processing Company (RASCO) | LLDPE | Lanufene |
| LEXAN™ 131P resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Sylvin 8880-70 LG Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |