Generic PESU
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U7VbfS_Generic-PESU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PESU This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.36 - 1.37 | g/cm³ | ASTM D792 |
| 23°C | 1.37 - 1.39 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (380°C/2.16 kg) | 20 - 75 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.60 - 0.91 | % | ASTM D955 |
| 23°C | 0.69 - 0.90 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.42 - 0.60 | % | ASTM D570 |
| 23°C, 24 hr | 0.10 - 0.91 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.76 - 1.0 | % | ISO 62 |
| Solution Viscosity | 449 - 818 | mPa·s | ASTM D445 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2540 - 3070 | MPa | ASTM D638 |
| 23°C | 2580 - 3030 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 23°C | 78.0 - 91.6 | MPa | ISO 527-2 |
| Fracture, 23°C | 53.0 - 90.0 | MPa | ISO 527-2 |
| 23°C | 82.0 - 91.6 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 4.7 - 7.1 | % | ASTM D638 |
| Yield, 23°C | 5.9 - 7.0 | % | ISO 527-2 |
| Fracture, 23°C | 3.0 - 62 | % | ASTM D638 |
| Flexural Modulus | |||
| 23°C | 2280 - 2800 | MPa | ASTM D790 |
| 23°C | 2000 - 3000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 110 - 128 | MPa | ASTM D790 |
| 23°C | 115 - 131 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 - 6.5 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 43 - 93 | J/m | ASTM D256 |
| 23°C | 4.3 - 8.9 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 199 - 205 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 188 - 210 | °C | ISO 75-2/A |
| Glass Transition Temperature | 220 | °C | ASTM E1356 |
| CLTE - Flow | |||
| -- | 4.8E-5 - 5.5E-5 | cm/cm/°C | ASTM D696 |
| -- | 4.7E-5 - 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+4 - 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 14 - 18 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 3.50 - 3.54 | ASTM D150 | |
| Dissipation Factor | |||
| 23°C | 1.7E-3 - 5.7E-3 | ASTM D150 | |
| 23°C | 1.7E-3 - 0.014 | IEC 60250 | |
| Comparative Tracking Index | 100 - 125 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 - 177 | °C | |
| Drying Time | 2.5 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.050 | % | |
| Rear Temperature | 349 - 371 | °C | |
| Middle Temperature | 365 - 371 | °C | |
| Front Temperature | 359 - 377 | °C | |
| Nozzle Temperature | 345 - 361 | °C | |
| Processing (Melt) Temp | 350 - 365 | °C | |
| Mold Temperature | 135 - 160 | °C | |
| Injection Pressure | 8.00 - 88.8 | MPa | |
| Back Pressure | 0.500 - 7.35 | MPa | |
| Screw Speed | 55 - 80 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PESUThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Aobang TPU-Polyester 85-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| SolVin 382NG | INOVYN | PVC, Unspecified | SolVin |
| Double Elephant SX-302 | Suzhou Double Elephant Optical Material Co., LTD. | Acrylic (PMMA) | Double Elephant |
| Eltex® TUB121N3000 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| KOCETAL® CF704 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |