SAMAT 5000AC
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | POLYROCKS CHEMICAL CO., LTD |
| Trademark: | SAMAT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U6OhqR_SAMAT-5000AC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAMAT™ 5000(+) are halogen-free flame retardant Polypropylene (PP) with phosphorus and nitrogen as the flame retardant elements. Carbonize and gaseous phase retardant mechanisms play the flame retardant performance. The flammability can reach UL94-V0 (0.75mm, 1.5mm and 3.0mm) and pass the water immersion test at 70°C for 168hrs (UL746C) and GWIT 750°C and GWFI 960°C. They have the characteristics of low density of finished products, low smoke and little corrosion to molds. 5000(+) pass UL tests and meet the requirements of RoHS, SVHC, PFOS&PFOA, 16P, Halogen-free and PAHs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength | 35.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 120 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1 | UL 746C, UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Flammability after water-boiling testing at 70°C for 168 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M3500CA (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Sindustris ABS LRS761 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| THERMOLAST® M TM7ADT (Series: MC/AD1) | KRAIBURG TPE | TPE | THERMOLAST® M |
| NuSil GEL1-8155 | NuSil Technology | Silicone | NuSil |
| Dynaflex™ G7980-9001-02 | PolyOne Corporation | TPE | Dynaflex™ |