NEXUS PC/PBT PC/PBT7804
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Nexus Resin Group, LLC. |
| Trademark: | NEXUS PC/PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U63Wpt_NEXUS-PC-PBT-PC-PBT7804.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Molding Grade PC/PBT |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.80 to 1.1 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 48.3 | MPa | ASTM D638 |
| Flexural Modulus | 1970 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 670 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 93.3 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 232 to 249 | °C | |
| Middle Temperature | 246 to 260 | °C | |
| Front Temperature | 246 to 266 | °C | |
| Nozzle Temperature | 246 to 266 | °C | |
| Processing (Melt) Temp | 252 to 274 | °C | |
| Mold Temperature | 48.9 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 75 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 2750 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Tenac™-C TFC84 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| AIE PA66 60G5F | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| Ingeo™ 4043D | NatureWorks® LLC | PLA | Ingeo™ |
| ESTOPLAST ZK 6002GY32 | Ester Industries Ltd. | PC | ESTOPLAST ZK |